► Ecoworld® Biodegradable Polymer
Ecoworld® Biodegradable Polymer can be broken down by microorganism into CO2, H2O and high quality organic fertilizers within 180 days under composting conditions without generating any poisonous gas. It is the main raw material for biodegradable plastic films which can help reducing white pollution.
►Technical Properties
Ecoworld® Biodegradable Polymer uses one-step polymerization technology during production. It corresponds with American and European food contact safety standards, EN13432 and ASTM6400D standards. Its shelf life is 12 months under the condition of being stored in sealed packages. It can ensure a storage life of 12 months after being processed into finished products.
|
|
Unit 单位 |
Blow MoldingGrade 吹塑级 |
|
Density 密度 |
g/cm³ |
1.26 |
|
Melting Point 熔点 |
℃ |
115 |
|
Vicat Softening Point 维卡软化点 |
℃ |
≥90 |
|
MeltingIndex 熔指（190℃ ,2.16kg） |
g/10min |
3-5 |
|
Carboxyl Content 酸值 |
mol/t |
≤30 |
|
Moisture 水份 |
% |
≤0.05 |
|
Ash Content 灰份 |
% |
≤0.1 |
|
Tensile Strength 拉伸强度 |
Map |
≥18 |
|
Elongation At Break 断裂伸长率 |
% |
≥500 |
Ecoworld® Biodegradable Polymer can be widely applied to the manufacturing of shopping bags, food packages, mulch films,garbage bags, etc.
►Ecowill® Biodegradable Polymer Compound
ECOWILL® is a family of modified Biodegradable Polymer Compound which are developed and manufactured by JinHui ZhaoLong. In contrast to conventional plastics, ECOWILL® allows its final plastic products to possess both biological ( biodegradable and compostable) and physical (printable and weldable) advantages at the same time. ECOWILL® has been widely applied to industrial and agricultural sectors, such as shopping bags, garbage bags, food packages and mulch films etc. Currently there are two series of products being included in ECOWILL® family which are ECOWILL® FS-0330 and ECOWILL® FP-0325 respectively.
ECOWILL® FS-0330 is Ecoworld® Biodegradable Polymer and starch compound. ECOWILL® FP-0325 is Ecoworld® Biodegradable Polymer and PLA compound. The compounds help to increase the tear strength and elongation of finished products greatly while not affecting the later processing. In addition, the compounds can reduce the product cost while still remain the biodogradable and composable properties
►Technical Properties
ECOWILL® FS-0330 Technical properties
|
PROPERTY 性能 |
UNIT 单位 |
TEST REFERENCE 测试依据 |
VALUE 数值 |
|
Melt Flow Rate 熔融指数 |
g/10min |
DIN ISO 1133 at T=160°C,W=5kg |
≤4 |
|
Density 密度 |
g/cm3 |
ISO 1183 |
1.26-1.3 |
|
Melting Temperature熔点 |
°C |
DSC |
110-120 |
|
Tensile strength 拉伸强度 |
% |
ASTM-D882 |
≥12 |
|
Elongation At Break 断裂伸长率 |
% |
ASTM-D882 |
≥180 |
ECOWILL® FP-0325 Technical properties
|
PROPERTY 性能 |
UNIT 单位 |
TEST REFERENCE 测试依据 |
VALUE 数值 |
|
Melt Flow Rate 熔融指数 |
g/10min |
DIN ISO 1133 at T=190°C,W=2.16kg |
3-5 |
|
Density 密度 |
g/cm3 |
ISO 1183 |
1.26-1.3 |
|
Melting Temperature熔点 |
°C |
DSC |
110-120 |
|
Tensile strength 拉伸强度 |
% |
ASTM-D882 |
22 |
|
Elongation At Break 断裂伸长率 |
% |
ASTM-D882 |
≥250 |
ECOWILL® FP-0615 Technical properties
|
PROPERTY 性能 |
UNIT 单位 |
TEST REFERENCE 测试依据 |
VALUE 数值 |
|
Melt Flow Rate 熔融指数 |
g/10min |
DIN ISO 1133 at T=190°C,W=2.16kg |
3-5 |
|
Density 密度 |
g/cm3 |
ISO 1183 |
1.26-1.3 |
|
Melting Temperature 熔点 |
°C |
DSC |
110-120 |
|
Tensile strength 拉伸强度 |
% |
ASTM-D882 |
≥18 |
|
Elongation At Break 断裂伸长率 |
% |
ASTM-D882 |
≥350 |